怎样选用腻子粉对付墙面裂缝?

来源: 日期:2021-07-21 发布人:juyehe

1、装修墙体裂缝:装修裂缝随地基的变动呈现不均匀的分布。这是由于装修墙体沉降变形造成的,解决办法:

1. Decoration wall cracks: Decoration cracks show uneven distribution with the change of foundation. This is caused by the settlement and deformation of the decoration wall
1)如果是装修建筑一直沉降变形、不要忙于修补,等待不再变形时再进行装修修补。
1) If the decoration building has been subsidence deformation, don't be busy with repair, wait for no longer deformation to repair.
2)装修修补要根据裂缝形状、密度大小而采取多种方案,可用开槽修补或者加网格布修补,必须用高弹腻子粉。
2) According to the shape and density of the cracks, a variety of schemes should be adopted for decoration repair. Slotting repair or mesh cloth repair can be used, and high elastic putty powder must be used.
2、装修粉刷层裂缝:找平砂浆柔性不够,表现为比较大的龟裂纹,一般是均匀的分布。用高弹腻子或双组份弹性腻子粉满批,分别修补。
2. Cracks in the decoration and painting layer: the leveling mortar is not flexible enough, showing relatively large cracks, which are generally evenly distributed. Use high elastic putty or two-component elastic putty powder for full batch repair.
3、装修保温层裂缝:一般呈现不规则的裂缝是比较常见。是由于苯板的收缩变形、网格布、砂浆、不正确的装修施工等很多原因造成的。解决办法应根据裂缝的大小及分布不同而定,如果比较严重,有必要加贴网格布或网布,如果不严重就用双组份的柔性腻子粉满批。
3. Decoration insulation layer cracks: generally irregular cracks are more common. It is caused by shrinkage deformation of benzene board, grid cloth, mortar, incorrect decoration construction and many other reasons. The solution should be determined according to the size and distribution of cracks. If it is serious, it is necessary to stick mesh cloth or mesh cloth. If it is not serious, use two-component flexible putty powder to fill the batch.
4、腻子层裂缝:一般表现为细微的龟裂纹,均匀分布,注意不是缝是纹,纹和缝是有区别的。
4. Putty layer crack: general performance for the subtle turtle crack, uniform distribution, attention is not seam is grain, grain and seam is different.